continue on to further improve, to make sure product top quality in line with market and consumer standard requirements. Our firm has a excellent assurance program have already been established for Silicone Masterbatch For Cable, Thermoplastic Elastomer Medical Grade TPE, Din Value Reducer, Customers' benefit and satisfaction are always our biggest goal. Please contact us. Give us a chance, give you a surprise.

China Wholesale Antiblock Slip Masterbatch Manufacturers – ANTI-WEAR AGENT NM-3C – Silike Detail:

Anti-abrasion masterbatch NM-3C is a pelletized formulation with 50% active ingredient dispersed in rubber . It’s particularly developed for rubber shoe’s sole compounds, helps to improving the final items abrasion resistance and decrease the abrasion value in the thermoplastics .

Compare to conventional lower molecular weight Silicone / Siloxane additives,like Silicone oil, silicone fluids or other type abrasion additives, SILIKE Anti-abrasion Masterbatch NM-3C is expected to give a much better abrasion resistance property without any influence on hardness and color.

Grade	NM-3C
Appearance	White pellet
active ingredients content %	50
Carrier	rubber
Melt index ( 190℃, 10.00KG ) g/10min	5.10 ( typical value )
Dosage % (w/w)	0.5～5%

(1) Improved abrasion resistance with decreased abrasion value

(2) Impart the processing performance and final items appearance

(3) Eco-friendly

(4) No influence on hardness and color

(5) Effective for DIN, ASTM, NBS , AKRON, SATRA, GB abrasion tests
…..

Applicable for NR, NBR, EPDM, CR, BR, SBR, IR, HR, CSM, etc.

Basic formula	NR/NBR	40	+NM-3C	0	2%	4%	6%
	Engine oil	5	DIN value	170	139	129	117
	CB	50

Mix NM-3C with rubber into internal mixer during the temperature rising mixture process, to evenly mix. The output temperature should be above 100 ℃. NM-3C is recommend to be used with Si-69.

When added to rubber at 0.2 to 1% , improved processing and flow of the resin is expected, including better mold filling, less extruder torque, internal lubricants, mold release and faster throughput; At a higher addition level , 2~10%, improved surface properties are expected, including lubricity , slip, lower coefficient of friction and greater mar/scratch and abrasion resistance

25Kg / bag , craft paper bag

Transport as non-hazardous chemical. Store in a cool , well ventilated place .

Original characteristics remain intact for 24 months from the production date , if kept in recommend storage.

Chengdu Silike Technology Co., Ltd is a manufacturer and supplier of silicone material, who has dedicated to R&D of the combination of Silicone with thermoplastics for 20⁺ years, products including but not limited to Silicone masterbatch , Silicone powder, Anti-scratch masterbatch, Super-slip Masterbatch, Anti-abrasion masterbatch, Anti-Squeaking masterbatch, Silicone wax and Silicone-Thermoplastic Vulcanizate(Si-TPV), for more details and test data, please feel free to contact Ms.Amy Wang Email: amy.wang@silike.cn

Product detail pictures:

FREE SILICONE ADDITIVES AND Si-TPV SAMPLES MORE THAN 100 GRADES

Sample type

50+
grades Silicone Masterbatch
10+
grades Silicone Powder
10+
grades Anti-scratch Masterbatch
10+
grades Anti-abrasion Masterbatch
10+
grades Si-TPV
8+
grades Silicone Wax

The customer service reprersentative explained very detailed, service attitude is very good, reply is very timely and comprehensive, a happy communication! We hope to have a opportunity to cooperate.